Sealing ability of MTA, CPM, and MBPc as root-end filling materials: a bacterial leakage study

ABSTRACT Objectives To evaluate the sealing ability of three root-end filling materials (white MTA, CPM, and MBPc) using an Enterococcus faecalis leakage model. Material and Methods Seventy single-root extracted human teeth were instrumented and root-ends were resected to prepare 3 mm depth cavities. Root-end preparations were filled with white MTA, CPM, and MBPc cements. Enterococcus faecalis was coronally introduced and the apical portion was immersed in BHI culture medium with phenol red indicator. The bacterial leakage was monitored every 24 h for 4 weeks. The statistical analysis was performed using the Wilcoxon-Gehan test (p<0.05). Results All cements showed bacterial leakage after 24 hours, except for the negative control group. The MBPc showed significantly less bacterial leakage compared with the MTA group (p<0.05). No significant differences were found between the CPM and the other groups. Conclusions The epoxy resin-based cement MBPc had lower bacterial leakage compared with the calcium silicate-based cements MTA and CPM.

Solubility and bacterial sealing ability of MTA and root-end filling materials

ABSTRACT Objective To evaluate solubility and sealing ability of Mineral Trioxide Aggregate (MTA) and root-end filling materials. Material and Methods The materials evaluated were: MTA, Calcium Silicate Cement with zirconium oxide (CSC/ZrO2), and zinc oxide/eugenol (ZOE). Solubility test was performed according to ANSI/ADA. The difference between initial and final mass of the materials was analyzed after immersion in distilled water for 7 and 30 days. Retrograde cavities in human teeth with single straight root canal were performed by using ultrasonic tip CVD 9.5107-8. The cavities were filled with the evaluated materials to evaluate sealing ability using the bacterial leakage test with Enterococcus faecalis. Bacterial leakage was evaluated every 24 hours for six weeks observing the turbidity of Brain Heart infusion (BHI) medium in contact with root apex. Data were submitted to ANOVA followed by Tukey tests (solubility), and Kruskal-Wallis and Dunn tests (sealing ability) at a 5% significance level. Results For the 7-day period, ZOE presented highest solubility when compared with the other groups (p<0.05). For the 30-day period, no difference was observed among the materials. Lower bacterial leakage was observed for MTA and CSC/ZrO2, and both presented better results than ZOE (p<0.05). Conclusion MTA and CSC/ZrO2 presented better bacterial sealing capacity, which may be related to lower initial solubility observed for these materials in relation to ZOE.

Sealing Ability of MTA Used as a Root End Filling Material: Effect of the Sonic and Ultrasonic Condensation

Despite the excellent properties of mineral trioxide aggregate (MTA), the condensation technique may have some influence in its sealing ability. The purpose of this study was to compare the sealing ability of sonic and ultrasonic setting of MTA. Thirty-four extracted human teeth had their canals prepared and filled with Sealapex sealer and gutta-percha using the active lateral condensation technique. The teeth were rendered waterproof and apicoectomy performed at 3 mm from the apex. Root-end cavities (3.0 mm deep and 1.4 mm diameter) were prepared with diamond ultrasonic tips. The root-end cavities were filled with Pro-Root MTA® with ultrasonic vibration, sonic vibration or no vibration. The positive control group did not receive any material while the negative control group was totally rendered waterproof. After material set, the specimens were immersed in Rodhamine B for 24 h, under vacuum in the first 15 min, then washed, dried and split longitudinally for evaluating the infiltration at the dentin/material interface. Data were analyzed using ANOVA and Tukey's tests at 5% significance level. Sonic vibration promoted the lowest infiltration values (p<0.05). It was concluded that sonic vibration could be considered an efficient aid to improve the sealing ability of MTA when used as root-end filling material.

Resumo O objetivo deste estudo foi avaliar in vitro, a influência da vibração sônica e ultrassônica no selamento marginal proporcionado pelo MTA. Trinta e quatro dentes humanos tiveram seus canais radiculares instrumentados e obturados com cimento Sealapex® pela técnica da condensação lateral ativa. Os dentes foram impermeabilizados e seccionados os 3 mm apicais. Retrocavidades (3 mm de profundidade e 1,4 mm de diâmetro) foram preparadas com pontas ultrassônicas diamantadas. As retrocavidades foram preenchidas com Pro-Root MTA® com auxílio da vibração ultrassônica, com auxílio da vibração sônica e sem vibração alguma. O grupo controle positivo não recebeu material retrobturador, enquanto que o negativo foi totalmente impermeabilizado. Após a presa do material, os espécimes foram mergulhados em Rodamina B por 15 min em vácuo, permanecendo nesta solução por mais 24 h. Em seguida, foram lavados, secados e clivados longitudinalmente para avaliação da infiltração do corante na interface dentina/material retrobturador. Os dados foram analisados utilizando a análise de variância e o teste de Tukey (p<0,05). Observou-se que apenas a vibração sônica foi diferente apresentando os menores índices de infiltração. Pode-se concluir que vibração sônica contribui com a melhora da capacidade de selamento marginal proporcionado pelo MTA quando empregado como material retrobturador. .

pH and calcium ion release evaluation of pure and calcium hydroxide-containing Epiphany for use in retrograde filling

OBJECTIVE: Hydroxyl (OH-) and calcium (Ca++) ion release was evaluated in six materials: G1) Sealer 26, G2) White mineral trioxide aggregate (MTA), G3) Epiphany, G4) Epiphany + 10 percent calcium hydroxide (CH), G5) Epiphany + 20 percent CH, and G6) zinc oxide and eugenol. MATERIAL AND METHODS: Specimens were placed in polyethylene tubes and immersed in distilled water. After 3, 6, 12, 24, and 48 h, 7, 14, and 28 days, the water was assessed for pH with a pH meter and for Ca++ release by atomic absorption spectrophotometry. RESULTS: G1, G2, G4, and G5 had the highest pH until 14 days (p<0.05). G1 presented the highest Ca++ release until 6 h, and G4 and G5, from 12 h through 14 days. Ca++ release was greater for G1 and G2 at 28 days. G6 released the least Ca++. CONCLUSIONS: MTA, Sealer 26, Epiphany, and Epiphany + CH release OH- and Ca++ ions. Epiphany + CH may be an alternative as retrofilling material.

Radiopacidade de novos biomateriais usados em cirurgia parendodôntica / Radiopacity of new biomaterials used in parendodontic surgery

Objetivo: Comparar a radiopacidade dos materiais retrobturadores: Cimento Portland (CP), Super EBA (SEBA), MTA-Angelus com Sulfato de Bário (MTA-SB), MTA-Angelus com Óxido de Bismuto (MTA-OB), MTA-Angelus (MTA-AC), Cimento Ionomérico Shofu (IV), PRO ROOT Dentsplay (PRO) e Óxido de Zinco Eugenol (OZE). Método: Cinco anéis metálicos de 10mm de diâmetro interno, com 1mm de espessura, foram preenchidos com cada um dos materiais, preparados conforme indicação dos fabricantes e radiografados juntos com o stepwedge proposto pela ANSI/ADA n. 53. Os filmes processados pelo método tempo/temperatura foram escaneados, sendo realizadas 3 análises da intensidade pixel (ip) para cada corpo de prova, num total de 15 leituras de cada material. Obtidas as médias, foram comparadas através do teste "F" de Snedecor, em análise de variância (ANOVA), onde F=16.63 (p=0,000) significativo ao nível de 1%. Adotou-se o nível de significância de 5% de probabilidade (p menor que 0,05). Resultados: Em relação ao stepwedge, o grupo CP apresentou ip inferior ao do degrau 3 do stepwedge; os grupos IV e MTA-SB exibiram ip entre a dos degraus 3 e 4, enquanto para os grupos SEBA, MTA-OB, MTA-AC, PRO e OZE foram superiores à ip do degrau 6 do stepwedge. Conclusão: Com base nos resultados obtidos e nas especificações mínimas ANSI/ADA foi possível concluir que o grupo CP não apresenta a radiopacidade mínima necessária para um cimento endodôntico, e que o IV e MTA-SB estão no limite da norma. Contudo, considerando as dimensões da cavidade a ser retro-obturada, o limite de degrau 3 parece ser insuficiente para a segura constatação da qualidade da retro-obturação.

Purpose: To study the radiopacity of retrograde fillings: Portland Cement (CP), Super EBA (SEBA), MTA-Angelus with barium sulfate (MTA-SB), MTA-Angelus with bismuth oxide (MTA-OB), MTA-Angelus (MTA-AC), Ionomer Cement Shofu (IV), PRO ROOT Dentsplay (PRO) and Zinc Oxide Eugenol (OZE). Method: Five metal bands with a 10mm internal diameter and 1mm thickness were filled with each one of the materials, prepared according to manufacturer specifications and radiographed together with the stepwedge proposed by ANSI/ADA n. 53. Films were processed by the time/temperature method and then scanned, and performed 3 analyses of pixel intensity (ip) for each specimen, in a total of 15 readings of each material. Obtained the means, they were compared with a Snedecor's F distribution in the analysis of variance (ANOVA) with F=16.63 (p=0.000) significant at 1% level. A 5% probability significance level (p less than 0.05) was adopted. Results: Regarding stepwed, considering the pixel intensity (ip), the CP group presented ip below step 3 stepwedge; the IV and MTA-SB groups showed ip between stepes 3 and 4, while for the SEBA, MTA-OB, MTA-AC, PRO and OZE groups, ip was above step 6 stepwedge. Conclusion: Based on the obtained results and the minimum ANSI/ADA specifications, it was possible to conclude that the CP group does not present the minimum radiopacity required from an endodontic cement, and that the IV and MTA-SB are at the standard's limit. However, considering the cavity dimensions to be retro-filled, the step 3 limit seems insufficient to find safe the retro-filling's quality.

Respuesta del tejido periapical de la rata al ProRoot MTA y a un cemento Portland modificado: un estudio metodológico / Periapical tissue response to ProRoot MTA and to a modified Portland cement in rats: a methodological study

Con el objeto de poner en contacto directo con los tejidos periapicales dos materiales a base de compuesto de minerales trióxido (ProRoot MTA y CPM) ampliamente sugeridos para ser utilizados como materiales de obturación retrógrada, se investigó la posibilidad de usar el conducto de la raíz distal del primer molar inferior como vía de acceso a éstos. Se utilizaron para ello 15 ratas Wistar de 250-300 g de peso. Luego de la apertura de al cámara pulpar, los conductos se instrumentaron hasta una lima #30 limitando su penetración hasta aproximadamente 3.5mm y hasta sentir la constricción por sensación táctil, acompañada por una irrigación constante con suero fisiológico. Los conductos del lado derecho e izquierdo se obturaron con CPM o ProRoot MTA respectivamente y las cavidades de acceso fueron selladas mediante doble capa de ionómero vítreo. El ánálisis histopatológico reveló que a los 7 días ambos materiales produjeron reacciones inflamatorias de tipo granulomatoso en los tejidos periapicales circundantes. A los 14 días, la intensidad de las reacciones inflamatorias, si bien algo irregulares, se mantuvo constante, aunque en general tendía a reducirse hacia el final de la experiencia. Los resultados demostraron que el conducto distal del primer molar inferior resultó ser una vía de acceso fácil para el acopio y contacto de materiales de obturaicón retrógrada con los tejidos periapicales de la rata. Sin embargo, a causa de la gran variabilidad anatómica y estructural del ápice radicular, el método requiere aún de un procedimiento más exacto para la determinación de la longitud de trabajo, permitiendo de esta forma una mejor adaptación de los materiales investigados en contacto con los tejidos periapicales.

Sealing ability of MTA and amalgam in different root-end preparations and resection bevel angles: an in vitro evaluation using marginal dye leakage

This in vitro study evaluated the effect of different apicoectomy angles, instruments used in root-end preparation, and dental materials used in retrofilling on apical sealing. Root ends were resected at 45 or 90 degrees in 80 single-rooted teeth. For each type of apicoectomy, root-end cavities were prepared with either a round carbide #2 bur or an S12/90D ultrasonic tip. The root-end cavities in each subgroup (apicoectomy + root-end preparation) were filled with silver amalgam without zinc (Am) or with gray mineral trioxide aggregate -Angelus (MTA), and the specimens were immediately immersed in 0.2 percent rhodamine B for 24 h. Sealing was evaluated based on the dyed cross-sectional dentin area. Data were analyzed statistically by the Kruskal-Wallis test at 5 percent significance level. No group showed complete sealing of root-end areas. The only significant factor affecting microleakage was dental material, with MTA exhibiting less leakage.

Este estudo in vitro avaliou o efeito de diferentes ângulos de apicectomia, instrumentos utilizados na retrocavitação e materiais odontológicos usados na retrobturação sobre selamento apical. Oitenta dentes unirradiculares, tratados endodonticamente, foram apicectomizados. Quarenta raízes tiveram seu ápice radicular seccionado com angulação de 45º e a outra metade com angulação de 90º. Para cada tipo de apicectomia realizou-se retrocavidades com broca esférica carbide nº 2 ou com retroponta ultra-sônica S12/90D. Cada subgrupo (apicectomia/retrocavidade) foi retrobturado com MTA ou amálgama, sendo os espécimes imediatamente imersos no corante Rodamina B a 0,2 por cento por 24 h. O selamento apical foi avaliado com base na área transversal de dentina corada ao redor da retrobturação. Os dados foram submetidos á análise estatística utilizando os testes de Kruskal-Wallis e Mann-Whitney. Nenhum grupo foi capaz de selar totalmente a região apical. O tipo de material utilizado na retrobturação foi o único fator que mostrou significativa diferença no selamento apical em relação à infiltração de corante.

CO2, Er: YAG and Nd: YAG lasers in endodontic surgery

OBJECTIVES: CO2, Er:YAG and Nd:YAG lasers have been used in endodontic surgery. This in vitro study evaluated 1 percent Rhodamine B dye penetration using computer-assisted morphometry (ImageTool Software®) of 108 endodontically treated human permanent canines. MATERIAL AND METHODS: Teeth were divided into 9 groups according to the technique used: A: 90-degree apicoectomy with bur, root-end cavity preparation with ultrasound and filled with MTA; B: 90-degree apicoectomy with bur, root-end cavity prepared with ultrasound and filled with MTA, and treatment of apical surface with CO2 laser (1 W, CW/CW); C: 90-degree apicoectomy with bur, and treatment of apical surface with Nd:YAG laser (150 mJ, 10 Hz); D: 90-degree apicoectomy with bur, and treatment of apical surface with CO2 laser,(1 W, CW/CW); E: apicoectomy with Er:YAG laser (400 mJ, 10 Hz), root-end cavity prepared with ultrasound and filled with MTA; F: apicoectomy with Er:YAG laser (400 mJ, 10 Hz) and treatment of apical surface with Nd:YAG laser (150 mJ, 10Hz); G: apicoectomy with CO2 laser (5W, CW/SP), root-end cavity prepared with ultrasound and filled with MTA; H: irradiation of apical end with CO2 laser (1 W, CW/CW); I: irradiation of apical end with Nd:YAG laser (150 mJ, 10 Hz). RESULTS: Dye penetration was found in all specimens at different rates, the lowest penetration occurring in groups C (16.20 percent), B (17.24 percent) and F (17.84 percent). CONCLUSIONS: Groups B, C and F represent the best technical sequences to perform endodontic surgery.

Estudo comparativo in vitro de quatro materiais odontológicos utilizados em retro-obturação apical / Comparative in vitro study of four dental materials used in retrograde apical filling

OBJETIVO: Esta pesquisa objetivou avaliar a capacidade de vedamento apical de quatro materiais odontológicos utilizados em retro-obturações. MATERIAL E MÉTODO: 80 dentes humanos (caninos superiores) foram tratados endodonticamente, apicectomizados e retrocavitados, seguindo-se criteriosamente os mesmos procedimentos técnicos; a amostra foi dividida aleatoriamente em quatro grupos (n = 20); em cada grupo a retro-obturação foi realizada utilizando-se um dos seguintes materiais: cianoacrilato de etila (CE); amálgama de Prata sem Zinco (AM); cimento de ionômero de vidro modificado por resina (CIVr); cimento de ionômero de vidro modificado por resina associado a fotopolimerização do material (CIVr+foto). Os espécimes foram imersos em azul de metileno a 0,2% por 24 horas a 37°C e seccionados longitudinalmente. A análise dos níveis de infiltração do corante foi realizada através da visualização das regiões vestibular e palatina/lingual das raízes dentárias. RESULTADOS: Os resultados foram submetidos à análise de variância SANES. A infiltração marginal foi menor no G2 (CE) seguida por G4 (CIVr+foto), G3 (CIVr) e G1 (AM), o qual apresentou o maior nível de infiltração. CONCLUSÃO: Nas condições do presente trabalho, o CIVr+foto e o CE apresentaram as melhores condições de vedamento apical.

OBJECTIVE: The objective of this study was to evaluate the apical sealing ability of four dental materials used in retrograde fillings. MATERIAL AND METHOD: Eighty human maxillary canines were selected and treated endodontically; the apical ends were sectioned and root-end cavities were prepared. The sample was randomly divided in four groups of 20 specimens each. In each group, root-end cavities were filled with one of the following materials: ethyl cyanoacrylate (EC); silver amalgam not containing zinc (AM); resin-modified glass ionomer cement (GIC); or resin-modified glass-ionomer cement and light curing (GIC+light). The specimens were immersed and kept in 0.2% methylene blue for 24 hours at 37oC and then sectioned longitudinally. The analysis of dye penetration was conducted by means of visual inspection of the buccal and lingual sections of the roots. RESULTS: Analysis of variance was used to compare results. The least marginal leakage was found in the EC group, followed by the GIC+light, GIC and AM groups, which had the greatest leakage. CONCLUSION: Apical sealing with GIC+light and EC provided the best apical sealing.

Avaliação, in vitro, da capacidade de selamento de obturações retrógradas realizadas com agregado de trióxido mineral e um cimento experimental / Sealing ability of mineral trioxide aggregate and an experimental cement used as retrofilling materials: an in vitro study

Avaliou-se a capacidade seladora de alguns materiais utilizados em obturações retrógradas, por meio da infiltração marginal de corante.Foram utilizados 34 incisivos centrais superiores humanos extraídos com raízes íntegras, cujos canais foram preparados biomecanicamente e obturados. Após 48 horas, realizou-se a apicectomia e confeccionou-se as cavidades retrógradas por meio de pontas ultra-sônicas. Após a impermeabilização das superficies externas das raízes, as mesmas foram divididas aleatoriamente em três grupos de 10, de acordo com os materiais retrobturadores, ou seja, o ProRoot-MTA, o MTA-Angelus e um cimento experimental (MBP-c). Após a retrobturação, as raízes foram imersas em solução aquosa de rhodamine B a 0,2 por cento por 48 horas. A impermeabilização externa foi removida e, então, realizou-se o desgaste longitudinal da face mesial radicular com disco de carburundum, expondo-se à retrobturação.

Effect of diode laser irradiation on the apical sealing of MTA retrofillings / Efeito da irradiação de laser de diodo no selamento apical em retrobturações com MTA

Apical sealing is essential for the success of paraendodontic surgery, so any procedure that may favor an adequate sealing of the apical remainder should be performed. The purpose of this study was to evaluate the influence of diode laser irradiation on the apical sealing of root-end cavities with MTA retrofillings. Root canals in twenty extracted human teeth were shaped with K-files and filled with gutta-percha. The apexes were cut off and root-end preparations were performed. The roots were divided randomly in 2 groups. Group 1 (ten specimens) was retrofilled with MTA. Group 2 was irradiated with diode laser, with 1 W for 20 seconds, on the apical surface and root end cavity before retrofilling with MTA. The specimens had their external surfaces impermeabilized with cyanoacrylate, except for the apical surface, and were then immersed in 1 percent rhodamine B dye for 72 h and placed in plaster stone. After that, the specimens were submitted to longitudinal abrasion until half of the root remained. The linear dye leakage was observed in these mid-roots between the root canal wall and retrofilling. The linear dye leakage was measured with Image Lab software, and the results were statistically analyzed with Student's t test. There were no statistically significant differences between the two groups (p > 0.05). The diode laser irradiation did not improve the apical sealing of MTA retrofillings under the conditions of this in vitro study.

O selamento apical é fundamental para o sucesso da cirurgia parendodôntica. Assim, procedimentos que melhorem o selamento do remanescente apical devem ser utilizados. O objetivo deste estudo foi verificar se a irradiação de laser de diodo poderia aumentar o selamento apical em cavidades retrógradas obturadas com MTA. Foram utilizadas 20 raízes de dentes humanos extraídos que, após preparo com lima tipo K, tiveram seus canais obturados com guta-percha. Os ápices foram cortados e sofreram preparo de cavidades retrógradas. As raízes foram divididas aleatoriamente em 2 grupos. O grupo 1 (dez espécimes) foi retrobturado com MTA, e o grupo 2 sofreu irradiação de laser de diodo na potência de 1 W por 20 s na superfície apical e na cavidade retrógrada antes da obturação com MTA. Os espécimes foram impermeabilizados externamente com cianoacrilato, com exceção da superfície apical, imersos em corante rodamina B a 1 por cento por 72 h, incluídos em gesso e posteriormente desgastados no sentido longitudinal até obter-se metade da raiz. Foi feita a leitura da infiltração linear do corante nessas hemi-raízes, entre a parede do canal radicular e a retroobturação, com auxílio do programa de computação Image Lab. Os resultados foram analisados estatisticamente pelo Teste t de Student. Não houve diferença estatística significante entre os dois grupos (p > 0,05). A irradiação com laser de diodo não proporcionou aumento do selamento apical em retrobturações com MTA sob as condições do presente estudo in vitro.

Avaliação da capacidade seladora apical de materiais retrobturadores empregando corante rodamina B / Evaluation of apical sealing ability of root-end filling materiais using rhodamine B Ink

Tem sido demonstrada a incompatibilidade de materiais alcalinos com a solução corante de azul de metileno utilizada em testes de infiltração marginal. O objetivo deste estudo foi avaliar a capacidade de selamento apical de materiais retrobturadores utilizando como solução corante a Rodamina B. Quarenta e cinco caninos humanos extraídos tiveram seus canais radiculares instrumentados e obturados. Após a secção da porção apical, cavidades retrógadas foram preparadas e os dentes divididos aleatoriamente em três grupos experimentais (n=13). Foram utilizados os seguintes materiais retrobuturadores: grupo 1 - cimento Sealer; grupo 2 - cimento de óxido de zinco e eugenol (OZE); grupo 3 - MTA - Angelus de presa rápida. Em seguida, os dentes foram imersos por 48 horas em solução de Rodamina B a 0,2 porcento tamponada, em ambiente com vácuo. Decorrido este período, as raízes foram seccionadas longitudinalmente e a infiltração do corante analisada em perfilômetro. Os grupos controle positivo e negativo apresentaram infiltração máxima ou zero respectivamente. Os resultados obtidos foram submetidos à análise estatística demonstrando que o Sealer 26 apresentou infiltração marginal menor que os demais materiais (p<0,05). O OZE e MTA Angelus apresentaram capacidade seladora semelhante (p<0,05). Conclui-se que o Sealer 26 apresenta capacidade seladora superior ao OZE MTA Angelus quando avaliado em solução de Rodamina B

Sealer penetration and marginal permeability after apicoectomy varying retrocavity preparation and retrofilling material

Apicoectomy failure is generally related to inappropriate marginal sealing of the retrocavity, which allows percolation of microorganisms and their products from root canal system to periapex. This study evaluated tubular penetration of canal sealers and marginal permeability after retrocavity irradiation with Er;Cr:YSGG laser and retrofilling with MTA or cyanoacrylate. Twenty-two single-rooted teeth were decoronated and endodontically treated, their apical 3 mm were resected and the root ends were retroprepared with a low-speed bur. Twenty roots were randomly assigned to 4 groups (n=5): GI and GII - retrofilling with MTA and cyanoacrylate, respectively; GIII and GIV - retrocavity irradiation with Er;Cr:YSGG laser (2.78 æm, 4 W, 20 Hz, 70.8 J/cm²) and retrofilling with MTA and cyanoacrylate, respectively. The remaining 2 roots served as positive and negative controls. The analysis of rhodamine B dye infiltration (p=0.05) demonstrated that laser irradiation and MTA retrofilling presented significantly higher permeability rates (p<0.05). Retrofilling with cyanoacrylate showed significantly lower permeability, either when laser was used or not on retrocavity. SEM analysis depicted more cyanoacrylate penetration through dentinal tubules when compared to MTA, suggesting a more efficient marginal sealing. Based on these results, it may be concluded that cyanoacrylate provided a less permeable retrofilling regardless of the retropreparation method, suggesting a more favorable condition to the establishment of the periapical healing.

O insucesso das cirurgias apicais é geralmente atribuído ao selamento marginal inadequado das retrocavidades, caracterizado pelo contato ineficiente entre o material retrobturador e a superfície dentinária, o que acaba por permitir a percolação de microorganismos provenientes do canal radicular para a região do periápice. Este trabalho teve como objetivos a análise da penetrabilidade tubular de materiais retrobturadores e a avaliação da permeabilidade marginal dentinária após irradiação das retrocavidades com laser de Er;Cr:YSGG e retrobturação com MTA ou cianoacrilato. Vinte e dois dentes humanos unirradiculares tiveram a coroa seccionada, foram tratados endodonticamente e tiveram os 3 mm apicais removidos. As retrocavidades foram preparadas com broca em baixa rotação. Vinte raízes foram aleatoriamente divididas em 4 grupos (n=5): GI e GII - retrobturação com MTA e cianoacrilato, respectivamente; GIII e GIV - retrocavidades irradiadas com laser de Er;Cr:YSGG (2,78 æm, 4 W, 20 Hz, 70,8 J/cm²) e retrobturação com MTA e cianoacrilato, respectivamente. As duas raízes restantes atuaram como controles positivo e negativo. A análise da infiltração do corante rodamina B (p=0,05) demonstrou que a irradiação com laser e a retrobturação com MTA apresentaram níveis de permeabilidade significantemente maiores (p<0,05). A retrobturação com cianoacrilato proporcionou níveis de permeabilidade significantemente menores em ambas as situações (EDTA-T ou laser). A análise das micrografias revelaram maior penetração tubular do cianoacrilato quando comparado ao MTA, indicando um selamento marginal mais eficiente. De acordo com os resultados obtidos, foi possível concluir que o cianoacrilato promoveu uma menor permeabilidade da retrobturação, independentemente do método utilizado para o retropreparo, sugerindo, portanto, uma condição mais favorável ao estabelecimento da reparação periapical.

[Evaluation of apical microleakage in cavity preparation with different dimension for retrograde filling]

Several materials are recommended for retrofilling. One of the best materials that have ever been suggested is MTA [Mineral Tioxide Aggregate]. Many studies have confirmed the biocompatibility, proper marginal adaptation and sealability of this agent. The purpose of this study was the evaluation of apical evaluation of apical microleakge in cavity preparation with different dimension for retrograde. In this study, we examined the influence of cavity dimension on sealability of MTA. We selected sixty roots with a single canal. After cleaning and shaping, the canals were obturated with guta-percha and canal sealer by lateral condensation technique. Samples were divided into 5 groups: two positive and negative control groups and three experimental groups. Cavity preparation was performed for all experimental groups with the following methods: A: 1.5mm depth and 0.6mm width B: 3mm depth and 0.6mm width C: 3mm depth and 1.5mm width After cavity preparation, MTA powder was placed in each cavity and wet cotton adjacent to them for 24 hours. Then the samples were placed in Incubator [37 degree C and 100% wet] for 72 hours. Subsequently dye penetration examination was performed; dye leakage was measured by stereomicroscope. We used T-test for statistical analysis. After statistical analysis these results were achived: 1. Increase depth from 1.5mm to 3mm reduce the amount of leakage. 2. No significant difference between leakage of cavities with different width was found [P-value>0.05]. It's better to prepare cavities for retrograde filling with more depth and less width

Avaliação, in vitro, da capacidade de selamento de obturações retrógradas realizadas com agregado de trióxido mineral e um cimento experimental / Sealing ability of mineral trioxide aggregate and an experimental cement used as retrofilling materials: an in vitro study

Avaliou-se a capacidade seladora de alguns materiais utilizados em obturações retrógradas, por meio da infiltração marginal de corante.Foram utilizados 34 incisivos centrais superiores humanos extraídos com raízes íntegras, cujos canais foram preparados biomecanicamente e obturados. Após 48 horas, realizou-se a apicectomia e confeccionou-se as cavidades retrógradas por meio de pontas ultra-sônicas. Após a impermeabilização das superficies externas das raízes, as mesmas foram divididas aleatoriamente em três grupos de 10, de acordo com os materiais retrobturadores, ou seja, o ProRoot-MTA, o MTA-Angelus e um cimento experimental (MBP-c). Após a retrobturação, as raízes foram imersas em solução aquosa de rhodamine B a 0,2% por 48 horas. A impermeabilização externa foi removida e, então, realizou-se o desgaste longitudinal da face mesial radicular com disco de carburundum, expondo-se à retrobturação.

Effect of different dye solutions on the evaluation of the sealing ability of mineral trioxide aggregate

Tem sido demonstrada a incompatibilidade de materiais alcalinos com a solucão corante de azul de metileno utilizada em testes de infiltracão marginal. O objetivo do presente estudo foi analisar a influência de diferentes solucões corantes na avaliacão do selamento apical proporcionado pelo agregado de trióxido mineral. Cinqüenta e seis caninos humanos extraídos tiveram seus canais radiculares instrumentados e obturados. Após a seccão da porcão apical, cavidades retrógradas foram preparadas e os dentes divididos aleatoriamente em quatro grupos experimentais (n = 13) e dois controles (n = 2). Foram utilizados os seguintes materiais retrobturadores: grupos 1 e 2 - Pro Root MTA (Dentsply); grupos 3 e 4 - cimento de óxido de zinco e eugenol (OZE). Em seguida, os dentes dos grupos 1 e 3 foram imersos em solucão de Azul de Metileno a 2% e dos grupos 2 e 4 em solucão de Rodamina B a 0,2% por 48 horas em ambiente com vácuo. Decorrido este período, os dentes foram seccionados longitudinalmente, e a infiltracão marginal foi analisada. Os dados obtidos foram submetidos à análise estatística (Análise de variância e teste de Tukey). Os resultados demonstraram que o Grupo 1 apresentou menor infiltracão apical que os demais (p < 0,05). Conclui-se que a avaliacão da capacidade seladora do MTA é influenciada pela solucão corante, uma vez que o mesmo apresentou melhores resultados com o Azul de Metileno e infiltracão marginal semelhante à do OZE quando avaliado em solucão de Rodamina B.

Microfiltración bacteriana, citotoxicidad y respuesta del periápice al MTA, al IRM, al super EBA y a la amalgama: una revisión / Bacterial microleakage, cytotoxicity and periapical response to MTA, IRM, super EBA and amalgam: a review

El propósito de esta revisión es establecer parámetros claros de cuáles métodos son los más adecuados para el estudio de la microfiltración, de la citotoxicidad y de la respuesta del periápice al MTA, la amalgama, el super EBA y el IRM como materiales de retroobturación, pues existen diversos métodos empleados en estas investigaciones, dentro de los cuales hay muchos que no ofrecen respuestas satisfactorias, ya sea porque son análogos con la clínica o por limitaciones intrínsecas de la prueba. La función principal de un material de obturación retrógrada es ofrecer sellado apical, para prevenir la colonización bacteriana y la difusión de sus productos desde el conducto a los tejidos periapicales. Las pruebas de microfiltración, citotoxicidad y los tests de implantación son las más empleadas en el estudio de estos materiales, pues a través de ellas se busca evaluar la compatibilidad con los tejidos y su capacidad de sellado. Las características de sellado, la adaptación marginal, las pruebas de citotoxicidad in vitro y las pruebas de uso e implantación en animales experimentales son altamente significativas para eliminar materiales con grados inaceptables de filtración y pobre biocompatibilidad. Estas pruebas son prerrequisitos y no sustitutos de estudios clínicos. La comparación clínica de los materiales de obturación retrógrada bajo condiciones similares quirúrgicas y postoperatorias debe ser el método más relevante para la evaluación del uso clínico y de su eficiencia a largo plazo

Avaliaçäo in vitro da capacidade seladora do super-EBA e do MTA em quatro técnicas de obturaçäo retrógrada / In vitro evaluation of the sealing ability of the super-EBA and MTA in four different types of retrograde filling

Avaliou-se a capacidade de selamento apical de quatro técnicas de vedamento retrógrado, empregando-se o Super-EBA e o MTA como materiais retrobturadores. A metodologia utilizada foi infiltraçäo apical com o uso do corante rhodamine B a 0,2 por cento em obturaçöes retrógradas em raízes de dentes extraídos. Os resultados mostraram que nas técnicas onde o Super-EBA foi utilizado näo ocorreu diferença estatística significante entre elas; quando o MTA foi utilizado como material retrobturador, houve diferença estatística significante entre as técnicas de obturaçäo retrógrada e canalizaçäo (p<0,05) e entre as técnicas de retroinstrumentaçäo com retrobturaçäo associada à obturaçäo retrógrada e canalizaçäo (p<0,05); näo houve diferença estatística significante entre os materiais retrobturadores Super-EBA e MTA empregados nas diferentes técnicas cirúrgicas estudadas